Rapid Hardening Cement (42.5)

Introduction
The product obtained by grinding cement clinker obtained by roasting suitable raw material, consisting essentially of anhydrous calcium sulphoaluminate and dicalcium silicate. Suitable gypsum and 0-10% limestone shall be blended with clinker during manufacture of rapid-hardening sulphoaluminate cement. The rapid-hardening cement product is hydraulicity binding material. It has high early strength. The code no is R-SAC and with four grades.
Properties

 

1)     High early strength and high strength properties

         Its compressive strength can reach 35-50Mpa within 1 day, 50-70Mpa after 3 days, and it also can grows continually

         with the increasing of curing age.

2)     High froze-resistance property:

         If used at the temperature as low as 0-10℃,which early strength is 5-6 times than that of OPC; if used in 0-20℃ with

         little admixture, its strength in 3-7d can reach 70-80% of designed strength, with very little strength loss after 300 times

         of froze-thaw circle.

3)     High impermeability:

         Because of its dense structure, the impermeability of the concrete is 2-3 times than that of OPC in same grade.

4)     Anti-carbonation property:

         It has good anti-carbonation property, and low dry-shrinkage.

5)     Corrosion-resistance:

         Rapid-hardening cement has good corrosion-resistance quality, especially much better in seawater corrosion

         resistance than that of high anti-sulphate Portland cement, with more than 1 corrosion-resistance coefficient.

  • Data

     

    Specific surface area(m2/kg): ≥350

    Setting time(min):

    Initial setting time: ≥25

    Final setting time: ≤180

     (Remark: the setting time can be adjusted according to the customer’s demand.)

    Strength data in different ages:

     

    Grade

    Compressive strength (Mpa)

    Bending strength (Mpa)

    1d

    3d

    28d

    1d

    3d

    28d

    42.5

    33.0

    42.5

    45.0

    6.0

    6.5

    7.0

    52.5

    42.0

    52.5

    55.0

    6.5

    7.5

    7.5

    62.5

    50.0

    62.5

    65.0

    7.0

    7.5

    8.0

    72.5

    56.0

    72.5

    75.0

    7.5

    8.0

    8.5

  • Application

     

    1.       Construction in winter.

    2.       Urgent repairs and rapid construction.

    3.       Spraying anchor and supporting engineering.

    4.       Water conservancy facilities and offshore projects.

    5.       Bridge and road construction.

    6.       Cement products and prefabricated components.

    7.       Industrial and civil engineering.

Method

Storage
Bulk and weave package with membrane, 50kg per bag, conservation in cool and dry place, prevent wet.
Images

◇  Shenyang telecommunication hub

◇   Capital airport landing field project, finished 6000 square meters within one week adopting rapid hardening CSA cement, and put into service after pouring 3 days.

◇   The national stadium (The bird’s nest)

◇   QinHuangdao Dock and seaport anti-corrosion project

Download

Online Service - English

Simon Mu:
Jack Young:
Julia Zhou:

Online Service - Russian

Цянь бинь Чжоу: